Enhanced photoactivity of Cu-deposited titanate nanotubes for removal of bisphenol A
Authors: Ruey-an Doong, Sue-min Chang, Chia-wei Tsai
Abstract:
One-dimensional nanotubes are promising nanostructured materials for a wide variety of environmental applications. In this study, the Cu-deposited titanate nanotubes (TNTs) were fabricated using an alkaline hydrothermal method at 150 ◦C and then 0.5–2 wt% Cu(II) ions were photodeposited onto the calcined TNTs at 500◦C for enhanced photodegradation of bisphenol A (BPA) under illumination of 365 nm UV light. The as-synthesized TNTs showed tubular structures with the outer diameter and inter-layer spacing of 7–10 and 0.8 nm, respectively. The X-ray absorption near-edge spectral results provided a strong support on the partially structural change from layered trititanate to anatase TiO2 through the distortion of octahedral TiO6 unit at 500 ◦C and the production of mixture of CuO and Cu2O after photodeposition of Cu ions, resulting in the formation of Cu-deposited TiO2/TNT nanocomposites to enhance the photocatalytic activity. A nearly complete removal of BPA by the Cu-deposited TiO2/TNTs was observed, and the pseudo-first-order rate constants (kobs) for BPA photodegradation by Cu-deposited TiO2/TNTs at pH 7.0 were 1.8–5.2 and 4.3–12.7 times higher than those of pure Degussa P25 and ST01 TiO2, respectively. In addition, the kobs for BPA photodegradation reached the maximum value of 0.253 ± 0.032 min−1 at 1 wt% Cu(II). The X-ray photoelectron spectra showed that the ratio of Cu2O to total Cu increased from 3.2% in the dark to 35.2% after illumination of 365 nm UV light for 5 min. In addition, electron paramagnetic resonance results indicated that the copper ions could serve as the electron mediators to prolong the retention time of photo-generated radicals, resulting in the enhancement of photodegradation efficiency and rate of BPA by Cu-deposited TiO2/TNTs.
Keywords:
Copper ions
Titanate nanotubes (TNTs)
Bisphenol A
Photodeposition
Photocatalytic activity
Published in: Applied catalysis B: Environmental (Volume 129, Pages 1-614, 17 January 2013)
Publisher: Elsevier
ISSN Information: 0926-3373
Enhanced photoactivity of Cu-deposited titanate nanotubes for removal of bisphenol A
- Vòng Sơ Khảo Cuộc Thi Đại Sứ Văn Hóa Đọc Năm 2024
- Ngày hội sách “CITTADELLA” khuyến khích và tôn vinh vai trò của sách trong sinh viên Bách khoa
- Cuộc Thi Ảnh “Khoảnh Khắc VNUHCM Libraries”
- Ngày hội Văn hóa đọc lần VI
- Ngày hội văn hóa đọc lần V
- Ngày hội văn hóa đọc lần II
- Ngày hội văn hóa đọc lần IV
- Ngày hội văn hóa đọc lần III
- Tiếp GS Omer Mert Denizci, Trường ĐH Marmara Thổ Nhĩ Kỳ
- Tiếp Cô Claudia Tarzariol Từ The University Of Trento, Italy (Unitrento)
- Tiến sĩ kiều bào Mỹ tặng sách trị giá 150.000 USD cho sinh viên bách khoa
- Khảo sát ý kiến bạn đọc
-
Trực tuyến:17
-
Hôm nay:6713
-
Tuần này:6713
-
Tuần trước:35200
-
Tháng trước:35200
-
Tất cả:4116580