Preparation and performance of Co based capsule catalyst with the zeolite shell sputtered by Pd for direct isoparaffin synthesis from syngas
Authors: Yuzhou Jin, Ruiqin Yang, Yasuhiro Mori, Jian Sun, Akira Taguchi, Yoshiharu Yoneyama, Takayuki Abe, Noritatsu Tsubaki
Abstract:
The mm-sized capsule catalyst Co/SiO2-Z with the H-type zeolite (HZSM-5) as the shell, and the Co/SiO2- Z-Sp-Pd capsule catalyst with Pd loaded by sputtering method, as well as the Co/SiO2-Z-IW-Pd capsule catalyst, loading the Pd by incipient wetness impregnation, were prepared and used for isoparaffin direct synthesis by Fischer–Tropsch synthesis reaction from syngas with H2/CO ratio of 2/1 at 1.0 MPa and 533K. The analysis results of XRD, SEM, EDS and NH3-TPD showed that a compact HZSM-5 shell was formed on the Co/SiO2 pellet, and the metallic Pd was well sputtered on the surface of the HZSM-5 shell for the Co/SiO2-Z-Sp-Pd catalyst. The isoparaffin and olefin selectivity increased in the FTS reactions on the HZSM-5 capsule catalyst than on the Co/SiO2 catalyst. The selectivity of isoparaffins increased, and the selectivity of olefins decreased when using the Co/SiO2-Z-Sp-Pd catalyst, compared with the Co/SiO2-Z catalyst or the Co/SiO2-Z-IW-Pd catalyst, because metallic Pd introduced by sputtering on the zeolite shell could hydrogenate olefins efficiently. It was suitable to use the sputtering method for the preparation ofthe zeolite capsule catalystloaded with metallic Pd, as conventional impregnation method could not reduce Pd cation due to the strong interaction from zeolite surface. The CO conversion, CH4and CO2 selectivity on the catalyst of Co/SiO2-Z-Sp-Pd increased with temperature increasing from 513K to 553K. At elevated temperature, the isoparaffin selectivity also increased while the olefin selectivity was suppressed.
Keywords:
Capsule catalyst
HZSM-5
Palladium (Pd)
Sputtering
Fischer–Tropsch synthesis (FTS)
Published in: Applied catalysis A: General (Volume 456, Pages 1-248, 10 April 2013)
Publisher: Elsevier
ISSN Information: 0926-860X
Preparation and performance of Co based capsule catalyst with the zeolite shell sputtered by Pd for direct isoparaffin synthesis from syngas
- Ngày hội Văn hóa đọc lần VI
- Vòng Sơ Khảo Cuộc Thi Đại Sứ Văn Hóa Đọc Năm 2024
- Ngày hội sách “CITTADELLA” khuyến khích và tôn vinh vai trò của sách trong sinh viên Bách khoa
- Cuộc Thi Ảnh “Khoảnh Khắc VNUHCM Libraries”
- Ngày hội văn hóa đọc lần V
- Ngày hội văn hóa đọc lần II
- Ngày hội văn hóa đọc lần IV
- Ngày hội văn hóa đọc lần III
- Tiếp GS Omer Mert Denizci, Trường ĐH Marmara Thổ Nhĩ Kỳ
- Tiếp Cô Claudia Tarzariol Từ The University Of Trento, Italy (Unitrento)
- Tiến sĩ kiều bào Mỹ tặng sách trị giá 150.000 USD cho sinh viên bách khoa
- Khảo sát ý kiến bạn đọc
-
Trực tuyến:28
-
Hôm nay:2499
-
Tuần này:26567
-
Tuần trước:40192
-
Tháng trước:59360
-
Tất cả:4048463