Spectroscopic characterization of Ni/Al2O3 catalytic materials for the steam reforming of renewables
Authors: Gabriella Garbarino, Serena Campodonico, Alvaro Romero Perez, Maria M. Carnasciali, Paola Riani, Elisabetta Finocchio, Guido Busca
Abstract:
Ni/alumina catalytic materials (with 0, 5, 16, 39, 125 and ∞ % wtNi/Wsupport, using a 5% silica-containing alumina with 170 m2/g surface area) have been characterized by XRD, IR, MicroRaman, UV–vis–NIR techniques. Three types of nickel oxide species have been identified: i) isolated Ni2+ species dispersed and strongly interacting with the support surface, predominant when the NiO coverage is well below that of the ‘theoretical monolayer’. (ii) Ni oxide-like particles having a vibrational environment similar to that of NiO nanoparticles, but with different Raman and UV spectra, predominant near or well above the ‘theoretical monolayer’. (iii) normal NiO particles at even higher Ni oxide contents, characterized by (2 M) magnonic and several phononic peaks in the Raman spectrum and normal position for the optical gap (absorption edge at ca. 300 nm). IR spectra of adsorbed CO recorded after reduction in hydrogen suggest that species i) predominantly gives rise to isolated Nio atoms, producing Nio polycarbonyls, while species ii) gives rise by reduction to Ni metal particles, over which unusually CO adsorbs producing only terminal species, without any formation of bridging CO species. This may be due to an unusual structure or morphology of these particles. The catalysts have been tested in the steam reforming of ethanol–phenol mixture as well as of pure ethanol. XRD, UV–vis–NIR and Raman studies show that the spent catalysts are largely reduced to metal with the appearance of hexagonal nickel, although unreduced or easily oxidixable centers are also detected.
Keywords:
Steam reforming of tars
Biomass tar
Ethanol steam reforming
Hydrogen production
Ni/Al2O3 catalysts
Catalyst deactivation
Raman spectroscopy
MicroRaman
Spectroscopy
IR spectroscopy
Nickel oxides
Electronic properties
Published in: Applied catalysis A: General (Volume 452, Pages 1-222, 15 February 2013)
Publisher: Elsevier
ISSN Information: 0926-860X
Spectroscopic characterization of Ni/Al2O3 catalytic materials for the steam reforming of renewables
- Ngày hội Văn hóa đọc lần VI
- Vòng Sơ Khảo Cuộc Thi Đại Sứ Văn Hóa Đọc Năm 2024
- Ngày hội sách “CITTADELLA” khuyến khích và tôn vinh vai trò của sách trong sinh viên Bách khoa
- Cuộc Thi Ảnh “Khoảnh Khắc VNUHCM Libraries”
- Ngày hội văn hóa đọc lần V
- Ngày hội văn hóa đọc lần II
- Ngày hội văn hóa đọc lần IV
- Ngày hội văn hóa đọc lần III
- Tiếp GS Omer Mert Denizci, Trường ĐH Marmara Thổ Nhĩ Kỳ
- Tiếp Cô Claudia Tarzariol Từ The University Of Trento, Italy (Unitrento)
- Tiến sĩ kiều bào Mỹ tặng sách trị giá 150.000 USD cho sinh viên bách khoa
- Khảo sát ý kiến bạn đọc
-
Trực tuyến:7
-
Hôm nay:733
-
Tuần này:733
-
Tuần trước:33572
-
Tháng trước:33572
-
Tất cả:4055468