Synthesis and characterization of low molecular weight poly(1-butene) macromolecules prepared using metallocene catalysts
Authors: J.L. Diez de Tuesta, E. Casas, J. Moreno, P. Perez Nebreda, J.M. Escola, R. Van Grieken
Abstract:
Poly(1-butene) low molecular weight macromolecules with molecular weights within 1000–20,000 g mol−1 and isotacticities around 50–90% were prepared by the polymerization of 1-butene in liquid phase with n-butane as solvent using two metallocene catalysts: rac-dimethyl-silyl-bis-(2-methyl-4,5-benzoindenyl)zirconium dichloride (A) and rac-dimethylsilyl-bis-(2-methylindenyl)zirconium dichloride (B). Catalyst A showed higher yields and productivities than catalyst B, as well as better isotacticity values, which were ascribed to the presence of an additional aryl substituent in the indenyl moiety which increases its stability and hinders deactivation phenomena by aggregation. Kinetic experiments with catalyst A showed a continuous increase in conversion along the time so no strong deactivation was observed. With catalyst A, an increase in the hydrogen pressure at 75◦C up to 6.0 bar led towards low molecular weight macromolecules with 3000–4000 g mol−1 and a isotacticity of 75–80%. An enhancement in temperature up to 105◦C decreased the yields, molecular weights and isotacticity for both catalysts. Additionally, increasing the hydrogen partial pressure to 1.0 bar at 95 and 105 ◦C decreased the molecular weight within the 3000–5500 g mol−1 range. XRD patterns of the majority of low molecular weight macromolecules showed the presence of mixed phases, although some low molecular weight macromolecules with pure phase I (twined hexagonal) were obtained. Additionally, the DSC thermograms showed a decrease in the melting temperatures of the crystalline phases of poly(1-butene) low molecular weight macromolecules with regard to the corresponding ones of poly(1-butene) polymers (Mw > 100,000 g mol−1), due to their lower molecular weight.
Keywords:
Metallocene
Low molecular weight macromolecules
Hydrogen
Poly(1-butene)
Published in: Applied catalysis A: General (Volumes 460–461, Pages 1-132, 10 June 2013)
Publisher: Elsevier
ISSN Information: 0926-860X
Synthesis and characterization of low molecular weight poly(1-butene) macromolecules prepared using metallocene catalysts
- Vòng Sơ Khảo Cuộc Thi Đại Sứ Văn Hóa Đọc Năm 2024
- Ngày hội sách “CITTADELLA” khuyến khích và tôn vinh vai trò của sách trong sinh viên Bách khoa
- Cuộc Thi Ảnh “Khoảnh Khắc VNUHCM Libraries”
- Ngày hội Văn hóa đọc lần VI
- Ngày hội văn hóa đọc lần V
- Ngày hội văn hóa đọc lần II
- Ngày hội văn hóa đọc lần IV
- Ngày hội văn hóa đọc lần III
- Tiếp GS Omer Mert Denizci, Trường ĐH Marmara Thổ Nhĩ Kỳ
- Tiếp Cô Claudia Tarzariol Từ The University Of Trento, Italy (Unitrento)
- Tiến sĩ kiều bào Mỹ tặng sách trị giá 150.000 USD cho sinh viên bách khoa
- Khảo sát ý kiến bạn đọc
-
Trực tuyến:17
-
Hôm nay:6905
-
Tuần này:6905
-
Tuần trước:35392
-
Tháng trước:35392
-
Tất cả:4116772